Epoxy Resin for Drain Pipe Repair Table

• Customization: Available
• Molecular Principal Chain: Other
• Color: Light Yellow
• Model NO.: M1008AB
• Shelf Time: 1 Year
• Appearance: Light Yellow Clear Liquid
• Transport Package: Drum
• Specification: A Grade Quality
• Origin: China
• HS Code: 35069120
• Production Capacity: 10000ton/Year

Product Description

Product Description

 

Epoxy resin 3560AB is an epoxy resin glue cured under normal temperature and low temperature conditions. It has anti-yellowing, strong adhesion, good fluidity, natural defoaming, low heat generation after mixing, greenhouse curing or heat curing; maximum casting thicknessis 10cm, mix up to 20KG each time at the room temperature is 25°C; maximum casting thickness is 15cm, mix up to 60KG each time when the room temperature is less than 20°C.
 

Applications

it is dedicated to the insulation of large pieces of crafts, river table and electronic potting and mold filling and other electronic parts, moisture-proof potting, secret sealing and so on.
 

Detailed Photos

 

Product Parameters

 

Hardening properties
                  Epoxy 3560A                    Harder3560B
Color: Colorless and transparent
Proportion: 1.15                                             0.96
Viscosity 25ºC: 1000-1500CPS            100-300MAXCPS
Conditions of Use
1)Ratio: A:B=100:33(weight ratio)
A:B=100:50(volume ratio)
2) Hardening conditions: 25ºC×72H- OR 55ºC×2H(100g)
3) Pot life: 25ºC×1 hour(100g)
Hardened property:
1) Hardness: shore D <80-83D
2) Withstand voltage: KV/mm 22
3) Bending strength: Kg/mm2 28
4) Volume resistance: Ohm3 1x10*15
5) Surface resistance: Ohmm2 5X10*15
6)Thermal conductivity:
W/M.K 1.36
7) Lure power loss: 1KHZ 0.42
8) Heat distortion temperature: ºC 90-100
9) Water absorption: % <0.15
10) Compressive strength: Kg/mm2 8.4

The above performance data is typical data measured in a laboratory environment with a
temperature of 25°C and a humidity of 70%. It is for customer reference only.

Give us a chance, and we' ll return you with satisfaction.