Low Density Fire Retardant Sheet Moulding Compound SMC for Automotive Parts

• Customization: Available
• Material: Composite Material
• Application: for Automotive Parts
• Model NO.: SMC5005D
• Fiber Content: 26%
• Color: Ral7021
• Width: 90cm
• Pressure: 5-15MPa
• Temperature: 145+/-5degree
• Maintaining Time: 1min/mm
• Load Weight: up to 40tons
• Shipment: by Refrigerator Container
• Transport Package: Carton and Pallet, Zig-Zag, 1000kg/Pallet
• Specification: A Grade
• Origin: China
• HS Code: 3921
• Production Capacity: 10000ton/Year

Product Description

Product Description

Description for SMC:
The formula is specially designed for products requiring low density, fire retardant and high strength.

The resin, thickening agent, release agent, filler, mixed high temperature curing agent, coating in the 2 film, the glass fiber filament after cutting machine cut into 25mm short strips, sprinkle in the coating resin paste film, the 2 layer composite thin film, from Finn and Fram, Inc From America kneading professional SMC sheet unit import, the glass fiber soaked through automatic packaging, folding machine, and then in the drying room temperature through thickening time, achieve the molding viscosity requirements, namely into finished products. Appearance: Zig-zag package, outside the aluminum film
Pressure MPa 5-15
Temperature º C 145± 5
Maintaining time: Min/mm 1.

we have other series SMC sheet, we export SMC to South East Asia, Europe, and Africa as well.

Technical Data:

 SMC5005D(Low Density)  

No	Item	Unit	Value	Testing standard
1	Density	g/cm^3	1.48	GB1463-05
2	Water absorption	mg	50	GB1462-05
3	Moulding shrinkage	%	0.05	GB/T15568-2008
4	HDT	ºC	≥200	GB1634-79
5	Fiberglass content	%	26	GB/T15568-2008
6	Flexural strength	MPa	140	GB1449-05
7	Tensile strength	MPa	55	GB1447-05
8	Impact strength	KJ/m^2	55	GB1451-05
9	Barcol hardness	/	41	GB/T3854-2005
10	Fire resistance	grade	V0	UL94

 