| Customization: | Available |
|---|---|
| CAS No.: | 26098-37-3 |
| Formula: | C8h4o3 C4h10o3 C4H2O3 C3h8o2 |
|
Still deciding? Get samples of US$ 2/kg
Request Sample
|
Suppliers with verified business licenses
Audited Supplier Audited by an independent third-party inspection agency
| Projects | Measured value | Test method |
| Solids content (%) | 62-68 | GB/T 7193-2008 |
| Viscosity (Pa.s, 25ºC) Brinell viscosity RVT sp#2/10 rpm | 0.5 0.95 | GB/T 7193.1-2008 |
| Curing 25ºC *0.5ml cobalt isooctanate solution and 0.5ml MEKP solution were added to 50g resin in air bath at 25ºC. | ||
| Gel time (min, 25ºC) | 9-11 | GB/T 7193.6-2008 |
| Exothermic peak | 180ºC | |
| Shelf life | 3months at 25ºC | |
| Curing resin | Measured value | Test method |
| Barcol Hardness | 40 | GB/T 3854 |
| Tensile strength (Mpa) | 75-80 | GB/T 2567 |
| Elongation (%) | 4 | GB/T 2567 |
| Bending Strength(Mpa) | 145 | GB/T 2567 |
| Bending Modulus(Gpa) | 4.9 | GB/T 2567 |
* Curing conditions at room temperature for 24 hours, 80ºC for 4 hours.
This information is based on GB/T7193 standard, according to the actual situation of the company and combined with the needs of users.
Since there are many variables in the process of using the product, it is suggested that users should conduct tests and experiments before using it.
Due to the increasing use of unsaturated polyester resins, some properties of the products may not be fully applicable to a particular use. We reserve the right to modify some technical parameters.
If users can't find the products they need or the problems they need to know in this 'Technical Data Sheet', please contact Fangxin company directly, and we will try our best to provide services according to the needs of users.
The unsaturated polyester resin products listed in this data are dangerous goods, which should be stored and transported in accordance with relevant national regulations.
Liquid unsaturated polyester resin is unstable.It should be stored in a cool place to avoid fire and isolate heat sources.It is advisable to finish it within three months below 25ºC.