Unsaturated Polyester Resin Used in FRP Products for Vehicle Parts

• CAS No.: 26098-37-3
• Formula: C15h14o8
• EINECS: 113
• Molecular Principal Chain: Element Organic Polymer
• Color: Transparent
• Solid Content: 72.0~77.0%
• Model NO.: FH-H-1238NW
• Acid Value: 19.0~29.0 Mgkoh/G
• Gel Time 25 Degree Min: 6.0 to 12.0min
• Flexural Modulus: 3800 MPa
• Tensile Strength: 70MPa
• Viscosity 25 Degree PA.S: 8000 to 10000 MPa.S
• Tensile Modulus: 3700MPa
• Impact Strength: 12kj/M2
• Transport Package: Drum
• Specification: A Grade Quality
• Origin: China
• HS Code: 39079100
• Production Capacity: 10000ton/Year

Product Description

Product Description

TW-Ga-1 is a high viscosity wax-free unsaturated polyester resin with good toughness and mechanical strength for FRP products. It is used in FRP products such as vehicle shells and vehicle parts.

Detailed Photos

 

 

Technical Data Sheet

 

1.Liquid resin technical data (25ºC)

Item	Unit	Test result	Test method
Appearance	---	Light yellow liquid	GB/T8237
Solid content	%	72.0~77.0	GB/T-7193-4.3
Acid value	mgKOH/g	19.0~29.0	GB/T 2895
Viscosity(mPa ·s)	mPa·s	8000~10000	JIS-K-6901-5.5.1
Gel time (min)	min	6.0~12.0	JIS-K-6901-5.9
Maximum exothermic temperature	ºC	>90	JIS-K-6901-5.9

Note: 25ºC gel time test ratio: 12% Co : 0.25% M-50:1.0%
 

2.Physical properties of casting body (for reference)

Item	Unit	Test result	Test method
Tensile Strength	MPa	70	GB/T2567
Tensile modulus	MPa	3700
Elongation at break	---	2. 5%
Flexural strength	MPa	130
Flexural modulus	MPa	3800
Impact strength	KJ/m^2	12
Barcol hardness	---	48	GB/T3854
Heat distortion temperature	ºC	76	GB/T1634

Note: 1) Sample making method according to GB/T8237; curing system: accelerator RCA 1.2%, curing agent Butanox M-50 2.0%.

1. Casting body after curing treatment: room temperature × 24 hours + 60 ºC × 3 hours + 90 ºC × 1 hour