80kg/M3 Density 1.18inch Thickness PVC Foam Flat Sheet for Harrypora/ Yachts/ Boats Building

• Customization: Available
• After-sales Service: Any Time
• Warranty: 6months
• Model NO.: P80-1.18inch
• Feature: Environmental, Light Weight
• Fire Rating: Other
• Certification: ISO9001
• Customized: Customized
• Material: PVC
• Property1: Impact Resistance
• Property2: Low Water Absorption
• Property3: Insulation
• Processing Temperture: -240 to +100degree
• Density: 45-250kg/M3
• Thickness: 30mm
• Transport Package: Carton, Pallet
• Specification: A Grade
• Trademark: UTEK
• Origin: China
• HS Code: 3921
• Production Capacity: 1000000m2/Month

Product Description

Product Description

PVC foam is a cross-linked rigid structural PVC foam material, as a close cell foam, based on vinyl polymer, modified with the throughout Aramids link. It is the compounding chemical material based on PVC and PUR. It is said as the cross-linked PVC foam core, in the international practice.

Properties

PVC foam is closed cell cross linked regid PVC foam, with excellent specific modulus and strength. PVC  foam core have outstanding fatigue properties, inpact resistance and low water absorption. It also has good insulation properties.PVC foam have both the good size stability and machinability, compatible with various sandwich structure processing methods, compatible with various resin systems. It is the ideal core material for te light weight high strength sandwich composite core material. The processing temperture ranges from -240ºC to +100ºC, the long term operation temperature ranges from -240ºC to +80ºC.Strucell P foam have good water resistance and not rotten. PVC foam have good fire resistance.UTEK series foam products can widely be used in wind energy, marine, sports, railway and aerospace industries. The density ranges 45-250 kg/m3.

Detailed Photos

 

Product Parameters

Item	Standard	Unit		P80
Density	ISO 845	Kg/m^3	msmv	80
Density(Nominal)	ISO 845	Kg/m^3	msv	72
Tensile strength	ASTM C297	Mpa	msv	2.5
Tensile strength	ASTM C297	Mpa	msmv	2.2
Tensile modulus	ASTM C297	Mpa	msv	95
Tensile modulus	ASTM C297	Mpa	msmv	85
Compressive strength	ISO 844	Mpa	msv	1.4
Compressive strength	ISO 844	Mpa	msmv	1.15
Compressive modulus	ISO 844	Mpa	msv	90
Compressive modulus	ISO 844	Mpa	msmv	80
Shear strength	ISO 1922	Mpa	msv	1.15
Shear strength	ISO 1922	Mpa	msmv	0.95
Shear modulus	ISO 1922	Mpa	msv	27
Shear modulus	ISO 1922	Mpa	msmv	23
Shear elongation,at break	ISO 1922	%	msmv	15
Shear elongation,at break	ISO 1922	%	msv	30
Heat resistance,%retention of shear strength,+60ºC	ASTM C393	%	/	>80
Water resistance,%retention of shear strength	ASTM C393	%	/	>80

 

Application

Strucell P can be used as the core material in the sandwich structure.
 