Glass Fiber Content Over 22% SMC Sheet Moulding Compound for Pressed Fiberglass Tray

• Customization: Available
• Material: Sheet Molding Compound
• Usage: Specialty Plastics
• Model NO.: SMC5001
• Plastic Forming Method: Lamination
• Color: White
• Application: for Fiberglass Tray
• Fiber Content: 22%-25%
• Width: 90cm
• Pressure: 5-15MPa
• Temperature: 145+/-5degree
• Maintaining Time: 1min/mm
• Transport Package: Carton and Pallet, Zig-Zag Packing, 1000kg/Pallet
• Specification: A Grade
• Origin: China
• HS Code: 3921
• Production Capacity: 10000ton/Year

Product Description

Product Description

Sanitary grade SMC gives finished products glossy  surface. It has low shrinkage and is water-resistant.

Item	Standard	Data	Remark
Density( g/cm³)	GB1463-88	1.82
Glass fiber content(%)	GB/T15568-95	≥22
Water  absorption(%)	GB1462-88	≤0.2
Average Shrinkage (%)	GB/T15568-95	≤0.02
Tensile Strength(Mpa)	GB1447-83	≥50
Flexural Strength(Mpa)	GB1449-83	≥120
Impact Strength( kJ/m²)	GB1451-83	≥50
HDT(ºC)	GB1634-79	≥200
Color	White

Introduce:
The resin, thickening agent, release agent, filler, mixed high temperature curing agent, coating in the 2 film, the glass fiber filament after cutting machine cut into 25mm short strips, sprinkle in the coating resin paste film, the 2 layer composite thin film, from Finn and Fram, Inc From America kneading professional SMC sheet unit import, the glass fiber soaked through automatic packaging, folding machine, and then in the drying room temperature through thickening time, achieve the molding viscosity requirements, namely into finished products. Appearance: Zig-zag package, outside the aluminum film

Usage:
Used for molding drinking water tank, automobile bumper, electrical products, bathroom products
Have smooth surface, beautiful color, high-strength, excellent insulating performance, anti-corrosion, high production efficiency. They are widely used in many fields such as electronics, electrical, auto parts, water tank, instrument, civil installation and decoration. Proper SMC/BMC should be selected according to product's structure, performance and mould.

Pressure MPa 5-15
Temperature º C 145± 5
Maintaining time: Min/mm 1.

Technical Data:

 

Type	Application
SMC-A (electric)	High mechanical strength products such as high/low voltage switch box, insulation plates
SMC-B (flame retardant)	High mechanical strength and flame retardant products such as signal lamps, cable tray
SMC-C (high-strength)	Special high mechanical strength products such as hammer handle
SMC-D (general purpose)	Non-electric products such as chair, water tank
BMC-A (electric)	Electric parts with common mechanical strength
BMC-D (general purpose)	Non-electric press mould products with common mechanical strength

 