| Customization: | Available |
|---|---|
| Shape: | 3D Fabric |
| Fiber Characteristics: | E-Glass |
|
Still deciding? Get samples of $ !
Request Sample
|
Suppliers with verified business licenses
Audited Supplier Audited by an independent third-party inspection agency
It is woven from E glass yarn and consists of two surface(deck) layers connected together by vertical links(piles).These links are woven together with the surface layers thus forming an integrated sandwich sructure.When a thermoset resin such as ployester or epoxy is added to the 3D glass fabric and lightly rolled,the surface fabric is impregnated with the resin.Capillary action also wets out the connecting links,so that when the fabric rebounds to its full height a hollow core is formed(much like the tree trunks in a forest).This one-step process forms a sandwich laminate that offers excellent strength,stiffness,light weight and durability.
During impregnation the fabric is compressed but immediately rebounds to its original height,resulting in a lightweight sandwich laminate.This sandwich laminateforms the basis of the most technology-advanced applications.The integral sandwich concept in which core and faces are integrated to build sandwich laminates from 3 to 22 mm.
Light weight, High stiffness
Simple and effective lamination process
Outstanding performance in resistance to delamination
Easy to make an angle curve
Hollow structure
High design-versatility
| Fabric type | E3HP | ||
| Resin type | Polyester | ||
| Laminate thickness | mm | 4.3 | |
| Core thickness | mm | 3.5 | |
| Face thickness | mm | 0.4 | |
| Roll quantity | m2 | 63.5 | |
| Roll length | m | 50 | |
| Roll width | mm | 1270 | |
| Fabric weight | kg/ m2 | 0.77 | |
| Resin weight | kg/ m2 | 0.86 | |
| Laminate weight | kg/ m2 | 1.63 | |
| Mechanical Properties: | |||
| Compressive strength | ASTM 365 | N/mm2 | 2.78 |
| Compressive modulus | ASTM 365 | N/mm2 | 40.9 |
| Shear strength | ASTM 273 | N/mm2 | 2.12 |
| Shear modulus | ASTM 273 | N/mm2 | 124 |
| Bending stiffness | ASTM 393 | N. m2 | 1.46 |
| Thermal Property: | |||
| Thermal conductivity | GB/T10294-1988 | W/(m.k) | 0.07 |