E Glass Fiberglass Direct Roving 1200tex 308h for Transparent LPG Cylinder

Product Details
Customization: Available
Shape: Roving
Fiber Characteristics: E-Glass
Still deciding? Get samples of US$ 0.74/kg
Request Sample
Diamond Member Since 2013

Suppliers with verified business licenses

Audited Supplier

Audited by an independent third-party inspection agency

High Repeat Buyers Choice
More than 50% of buyers repeatedly choose the supplier
Experienced Team
The supplier has 10 foreign trading staff(s) and 3 staff(s) with over 6 years of overseas trading experience
Fast Delivery
The supplier can deliver the goods within 15 days
Customization from Samples
The supplier provides sample based customization services
to see all verified strength labels (12)
  • E Glass Fiberglass Direct Roving 1200tex 308h for Transparent LPG Cylinder
  • E Glass Fiberglass Direct Roving 1200tex 308h for Transparent LPG Cylinder
  • E Glass Fiberglass Direct Roving 1200tex 308h for Transparent LPG Cylinder
  • E Glass Fiberglass Direct Roving 1200tex 308h for Transparent LPG Cylinder
  • E Glass Fiberglass Direct Roving 1200tex 308h for Transparent LPG Cylinder
  • E Glass Fiberglass Direct Roving 1200tex 308h for Transparent LPG Cylinder
Find Similar Products
  • Overview
  • Product Description
  • Product Features
  • Specification
  • Technical Data
  • Packaging
  • Storage
  • Detailed Photos
Overview

Basic Info.

Model NO.
E6CR17-1200-308H
Fiber Appearance
Continous Fiber
Glass Composition
E-Glass
Roving Type
Direct Roving
Other Specification
1200tex
Roll Weight
17kg
Type of Sizing
Silane
Transport Package
Roll with Pallet
Specification
A Grade Quality
Trademark
union
Origin
China
HS Code
70191200
Production Capacity
30000 Ton/Year

Product Description

Product Description
        308H direct roving is produced with the E6 glass formulation and coated with a silane-based sizing composition. It is specially designed for reinforcing epoxy resin and suitable for both amine and anhydride curing systems.
 
        308H sizing composition gives strong resin-to-glass bonding, which results in excellent mechanical and anti-fatigue properties of the end composites. The product is designed for the high tension winding process. Typical applications include small bore sucker rods, high pressure pipes, storage tanks and pressure vessels.
Product Features
·Good abrasion resistance under high tensions and smooth run-out
·High retention rate in boiling water
·Excellent mechanical properties and fatigue resistance
·Excellent acid corrosion resistance
Specification
Glass type E6
Sizing type Silane    
Typical filament diameter (um)
17 21 24
Typical linear density (tex)
600
1200
2400
2000
2400
4800
Example
E6DR17-2400-308H
 
Technical Data
Item
Linear density variation
Moisture content
Sizing content
Breakage strength
Unit % % %
N/tex
Test method
ISO 1889
ISO 3344
ISO 1887
ISO 3341
Standard range
± 5
≤ 0.10
0.55 ± 0.15
≥ 0.40
Mechanical properties
Unit Value Resin Test method
Tensile strength
MPa 2675
Amine/DER331
ASTM D2343
Tensile modulus
GPa 82.2
Amine/DER331
ASTM D2343
Shear strength
MPa 74
Amine/DER331
ASTM D2344
Strength retention(72 hr boiling)
%
> 96
Amine/DER331
/
 
Packaging
Item Unit Standard
Typical packaging method
/
Packed on pallets.
 
Typical package height
mm (in)
260 (10.2)
 
Package inner diameter
mm (in)
160 (6.3)
 
Typical package outer diameter
mm (in)
280 (11.0)
 
310 (12.2)
Typical package weight
kg (lb)
17 (37.5)
 
22 (48.5)
 
Number of layers
layer
3 4 3 4
Number of packages per layer
pcs
16 12
Number of packages per pallet
pcs 48 64 36 48
Net weight per pallet
kg (lb)
816 (1799.0)
1088 (2398.6)
792 (1746.1)
1056 (2328.1)
Pallet length
mm (in)
1140 (44.9)
 
1270 (50.0)
 
Pallet width
mm (in)
1140 (44.9)
 
960 (37.8)
 
Pallet height
mm (in)
940 (37.0)
1200 (47.2)
940 (37.0)
1200 (47.2)
Storage
        Unless otherwise specified, the fiberglass products should be stored in a dry,cool and moisture proof area.The best temperature and humidity should be maintained at -10ºC ~35ºC and ≤80% respectively. To ensure safety and avoid damage to the product, the pallets should be stacked not more than three layers high. When the pallets are stacked in two or three layers, special care should be taken to correctly and smoothly move the upper pallet.
Detailed Photos
E Glass Fiberglass Direct Roving 1200tex 308h for Transparent LPG Cylinder
E Glass Fiberglass Direct Roving 1200tex 308h for Transparent LPG Cylinder
E Glass Fiberglass Direct Roving 1200tex 308h for Transparent LPG Cylinder
E Glass Fiberglass Direct Roving 1200tex 308h for Transparent LPG Cylinder



Give us a chance, and we' ll return you with satisfaction. 

 

Send your message to this supplier

*From:
*To:
*Message:

Enter between 20 to 4,000 characters.

This is not what you are looking for? Post a Sourcing Request Now
Contact Supplier