Product Description
Fiberglass biaxial combination fabric EWF1100 is composed of biaxial roving(The weight of the warp yarn is 662g/m2 and the weight of the weft yarn is 450g/m2), stitched by polyester yarn, it is widely used in pultrusion, RTM process, and hand lay-up. It is very good for pipe repair. The min width is 20cm, and the maximum width is 260cm. It widely produces FRP products like boat hulls, truck bodies, pultrusion profiles, bus roofing, and so on.
Properties:
Multi-layer finished one time, decrease layer and enhance efficiency.
Providing the product with multi-directional mechanical strength.
Uniform weight distribution, stable quality, and easy to use.
Special soft glass fibre, fast resin penetration, various specifications.
Packing &Storage:
Each roll is covered by a polyethylene plastic bag, then placed into a carton,and set on pallet.
Each pallet stack 9 or 16 rolls.The pallet shall no be higher than 2 layers.
Product shall be placed under dryness condition and shall no be open the covering membrane until applying.
Product Parameters
Item |
Specification |
Test Method |
Result |
Mass per unit area (g/m2) |
1100±44 |
GB/T9914.3 |
1103 |
Tensile Strength (N/25mm) |
Warp |
≥2200 |
GB/T7689.5 |
3506 |
Tensile Strength (N/25mm) |
Weft |
≥2100 |
GB/T7689.5 |
3321 |
Moisture Content (%) |
≤0.20 |
GB/T9914.1 |
0.05 |
Combustible Matter Content (%) |
1-7 |
GB/T9914.2 |
1.8 |
Polyester Laminated Sheet Flexible Strength (Mpa) |
Standard State |
≥290 |
GB/T1449 |
/ |
|
Humid State |
≥220 |
GB/T1449 |
/ |