3mm Thickness 3D Fiberglass Fabric

• Customization: Available
• Shape: 3D Fabric
• Fiber Characteristics: E-Glass
• Model NO.: E3P
• Diameter of Filaments: 13um
• Fiber Appearance: Continous Fiber
• Glass Composition: E-Glass
• Core Thickness: 3mm
• Weight: 0.78kg/M2
• Transport Package: Carton with Pallet
• Specification: A Grade Quality
• Trademark: Union
• Origin: China
• HS Code: 70193100
• Production Capacity: 50000m2/Month

Product Description

It is woven from E glass yarn and consists of two surfac(deck) layers connected together by vertical links(piles).These links are woven together with the surface layers thus forming an integrated sandwich sructure.When a thermoset resin such as ployester or epoxy is added to the 3D glass fabric and lightly rolled,the surface fabric is impregnated with the resin.Capillary action also wets out the connecting links,so that when the fabric rebounds to its full height a hollow core is formed(much like the tree trunks in a forest).This one-step process forms a sandwich laminate that offers excellent strength,stiffness,light weight and durability.
During impregnation the fabric is compressed but immediately rebounds to its original height,resulting in a lightweight sandwich laminate.This sandwich laminateforms the basis of the most technology-advanced applications.The integral sandwich concept in which core and faces are integrated to build sandwich laminates from 3 to 22 mm.

FEATURES:
Light weight, High stiffness
Simple and effective lamination process
Outstanding performance in resistance to delamination      
Easy to make an angle curve
Hollow structure
High design-versatility

APPLICATIONS:
Double wall storage tanks, chemical storage tanks, aircraft, railway, automotive, decorative wall panels, billboard, industrial roofing and various applications in different fields.
 

Technical Data Sheet
Fabric type				E3P	E5P	E8P	E10P	E12P	E15P	E18P	E22P
Thickness
Core		mm		3.0	5.0	8.0	10.0	12.0	15.0	18.0	22.0
Face		mm		0.4	0.4	0.4	0.6	0.6	0.6	0.6	0.6
Weight
Fabric		kg/m2		0.78	0.83	0.92	1.34	1.42	1.51	1.58	1.74
Laminate		kg/m2		1.65	1.76	1.95	2.84	3.01	3.20	3.35	3.60
Mechanical properties
Compressive strength	ASTM 365	N/mm2	Average	11.2	3.04	2.25	1.01	0.941	0.871	0.527	0.421
Shear strength	ASTM 273	N/mm2	Average	4.65	1.35	1.42	0.352	0.338	0.249	0.188	0.161
Bending strength	ASTM 393	N/mm2	Average	144	89.8	71.7	47.4	40.2	21.7	18.5	16.8
Thermal property
Thermal conductivity	GB/T10294-1988	W/(m.k)		0.07	0.07	0.07	0.08	0.08	0.08	0.08	0.08

 
NOTE: The technical parameters are attained on the condition that the ratio of 3D perform to designated resin is 1:1.1, what's more, resins with different species, brand and different dosages makes a difference to the final mechanical properties. The mechanical performance in weft direction is better than those in warp direction.





 
Give us a chance, and we' ll return you with satisfaction.