| Projects | Measured value | Test method |
| Solids content (%) | 64 | GB/T 7193 |
| Viscosity (Pa.s, 25ºC) Brinell viscosity RVT sp#2/10 rpm | 1000 mPas | ISO 2555 |
| Curing 25ºC *100g resin +1.8g cobalt isooctanate (1% Co +) +2.0g MEKP(methyl ethyl ketone peroxide) solution | ||
| Gel time (min, 25ºC) | 5 | GB/T 7193 |
| Exothermic peak | 180ºC | |
| Shelf life | 3months at 25ºC | |
| Curing resin | Measured value | Test method |
| Barcol Hardness | 40 | GB/T 3854 |
| Tensile strength (Mpa) | 70 | GB/T 2567 |
| Tensile modulus(Mpa) | 3300 | GB/T 2567 |
| Elongation (%) | 4 | GB/T 2567 |
| Flexural Strength(Mpa) | 120 | GB/T 2567 |
| Flexural Modulus(Mpa) | 3400 | GB/T 2567 |
| HDT 1.8MPa(ºC) | 87 | GB/T 1634.2 |
* Curing conditions at room temperature for 24 hours, 80ºC for 4 hours.
It is highly recommended to store the resin in a room below 25ºC to avoid direct sunlight. Exceeding the storage conditions will affect the resin properties such as viscosity and gel time. The resin should be mixed thoroughly before use. Keep the barrel sealed to prevent moisture from entering, and tighten the lid.