Unsaturated Polyester Resin for Making Artificial Limb

• Surface Treatment: Smooth
• Color: Pink
• Product Categories: FRP Model
• Molding Method: Hand Lay-up Method
• Material: Resin
• Fiber Type: GFRP
• Model NO.: TM-51002
• Type: Polyester FRP
• Shelf Time: 6 Month
• Appearance: Red Purple Liquid
• Viscosity 25 Degree PA.S: 0.30~0.50
• Thixotropic Index: 1.4~2.8
• Tensile Strength (MPa): 65
• Elongation at Break: 3.5%
• Bending Strength (MPa): 110
• Bagol Hardness: 45
• Gel Time (Min, 25ºC): 12~20
• Transport Package: Drum
• Specification: A Grade Quality
• Trademark: SWANCOR
• Origin: China
• HS Code: 39079100
• Production Capacity: 10000ton/Year

Product Description

Product Description

51002 unsaturated polyester resin is a pre-accelerated, thixotropic resin . It has low viscosity, good wettability to glass fiber, thixotropy and good workability.  The final product has good mechanical strength and high Elongation rate. It is suitable for hand lay-up process for making clothing models and other various FRP products.



 

Technical Data Sheet

 Properties of Liquid Resin(25ºC):

Projects	Index	Test method
Appearance	Red purple liquid	GB/T 8237.6.1.1
Viscosity (Pa.s, 25ºC)	0.30~0.50	JIS K 6901.5.6
Thixotropic index	1.4~2.8	JIS K 6901.5.6
Gel time (min, 25ºC)	12.0~20.0	GB/T7193 4.6

*Gel time test: Curing agent Butanox M-50 1.5%


Properties of Resin Casting Bodies

Test Projects	Measured value	Test method
Tensile Strength (Mpa)	65	GB/T 2567-2008
Elongation at break	3.5%	GB/T 2567-2008
Bending strength (Mpa)	110	GB/T 2567-2008
Thermal Deformation Temperature (ºC)	71	GB/T 1634-2004
Bagol Hardness	45	GB/T 3854-2005

Packing Photos

Standard packing is 200 kg steel drum.

 

Applications

 9231 resin is used for fiberglass reinforced plastic (FRP), and widely used in famous yacht manufacturers for their excellent water resistance, impact strength and fatigue resistance. 

 

  

Give us a chance, and we' ll return you with satisfaction.