Epoxy Resin and Hardener 3296 Ab for Hand Lay up to Repair Pipes

• Customization: Available
• CAS No.: 25068-38-6
• Color: Transperant
• Model NO.: 3296AB
• IBC Packing: 1000kg
• Transport Package: Carton, Pallet
• Specification: 3296AB
• Origin: China
• Production Capacity: 20000ton/Year

Product Description

Product Description

3296A/BS/BW is a fast-curing epoxy resin system, consisting of an epoxy resin part 3296A and a modified amine hardener part 3296BS and BW. It has the advantages of low viscosity, fast defoaming, fast curing, and can be adapted to the curing  requirements under different temperature environments. The final product is light and transparent, with good gloss and excellent performance. It is suitable for the repair and potting of parts.

Features

Low mixing viscosity, fast defoaming, fast curing adapt to different temperature environment curing requirements

The cured product is light and transparent, with good gloss and excellent performance
 

Applications

Suitable for pouring and hand lay-up molding processes

Can be used for electronic potting, stone surface repair and civil construction cracks repair
 

Product Parameters

TYPICAL PROPERTIES OF SYSTEM COMPONETNS

3296A Liquid Epoxy Resin

Appearance Colorless transparent liquid

Viscosity(25ºC, cps)  2300-2800

Density(25ºC, g/cm³)  1.1-1.2

Epoxide equivalent(g/mol)  175-185

Shelf life(10ºC  sealed, month) 24

3296A liquid epoxy resin must be stored at room temperature.
The vessel should be kept sealed. If find crystallization or precipitation, it is recommended to heat the resin to 60-70°C and stir or shake it properly.
 

	3296BS	3296BW
		BW-1	BW-2
Appearance	Colorless	Colorless	Colorless
	transparent liquid	transparent liquid	transparent liquid
Viscosity (25ºC cps)	25-35	40-60	90-140
Density (25ºC g/cm^3)	0.95-1.05	0.95-1.05	0.95-1.05
Amine value (mgKOH/g)	450-480	420-470	480-530

3296BS/BW/BF liquid amine curing agent must be stored at
room temperature. The vessel should be kept sealed. It is very sensitive to water and temperature. Storage in a high humidity environment will greatly affect the reactivity of the system material and the final performance.

MIXING AND HANDLING

		3296A/BW
Property	3296A/BS	BW-1	BW-2
Recommended quality ratio	100:34±2	100:34±2	100:34±2
Mixing Viscosity (25 ºC,cps)	400-600	400-600	400-600
Mixing Density (25ºC,g/cm^3)	1.1-1.2	1.1-1.2	1.1-1.2
Working Life(min)	40-60@30ºC	40-60@30ºC	40-60@30ºC

The mixing ratio of the configuration must be strictly in accordance with the instructions. Add a small amount or a large amount of curing agent will not slow down or accelerate the reaction rate, but it can lead to an unchangeable incompletely cured state of the cured product. The resin and the curing agent must be completely mixed until there is no fibrous or turbid state in the mixed liquid, paying special attention to uneven mixing on the wall and the bottom of the vessel
VISCOSITY CHANGE PROFILES
Viscosity of main epoxy resin at the temperature of 20-60ºC
Test condition:constant temperature room 25ºC

EXOTHERMAL PROFILE

		3296A/BW
Property	3296A/BS	BW-1	BW-2
Test Temp. (ºC)	30	20	10
Time to Tmax (min)	40-60	45-65	60-80

100g resin curing exothermic curve at the temp. of 10-30 ºCis as follows:

GEL TIME (HOT PLATE)

Hot Plate Temp. (ºC)		Gel time (min)
	3296A/BS	3296A/BW-1	3296A/BW-2
60	18-20	10-12	8-10
80	7-8	4-6	3-5
100	4-5	1.5-2.5	1-2

PHYSICAL PROPERTY AFTER CURING

Property	3296A/BS	3296A/BW-1	3296A/BW-2	Test Standard
Solidification program	60ºC /1hr+80ºC/2hr	RT/24hr+ 80ºC/5hr	RT/24hr+ 80ºC/5hr	/
HDT(ºC)	65-75	75-85	65-75	ASTM D256-02
Tg(ºC)	80-90	90-100	80-90	DSC, mid-point method
Hardness	80-90D	80-90D	80-90D	GB/T531-1999
Tensile strength(MPa)	60-70	/	/	ISO 527
Tensile modulus (GPa)	2.9-3.2	/	/	ISO 527
Elongation at break(%)	7.0-10.0	/	/	ISO 527
Flexural strength (MPa)	110-120	125-135	115-125	ISO 178
Flexural modulus(GPa)	3.0-3.3	3.0-3.2	3.0-3.2	ISO 178

Detailed Photos