The battery separator tissue is chiefly used as the base material of lead acid battery separator.
It is raw material of glass fiber separator, PE+glass separator, PVC+glass separator.
Feature:
Good acid resistance, high porosity, small pore size, high liquid absorptivity and low electric resistance.
Good vibrating resistance, starting ability, few permanganate reducate and longer service life.
The surface is flat and smooth, with uniform thickness.
Capable of preventing short circuits and absorbing needed electrolyte.
Technical Data:
| Binder (%) |
Thickness (mm)10KPA |
MD (N/5cm) |
Acid resistance (%) ( 72hours) |
Acid resistance (%) (15mins) |
Wetting time(s) | Fe (%) |
Cl (%) |
| 16 | GBZ 0.3 | ≥60 | <3.00 | <2.00 | <5 | ≤0.008 | ≤0.003 |
| 16 | GBZ 0.4 | ≥80 | <3.00 | <2.00 | <5 | ≤0.008 | ≤0.003 |
| 15 | GBZ 0.5 | ≥100 | <3.00 | <2.00 | <5 | ≤0.008 | ≤0.003 |
| 15 | GBZ 0.6 | ≥120 | <3.00 | <2.00 | <5 | ≤0.008 | ≤0.003 |
| 15 | GBZ 0.7 | ≥140 | <3.00 | <2.00 | <5 | ≤0.008 | ≤0.003 |
| 13 | GBZ 0.8 | ≥160 | <3.00 | <2.00 | <5 | ≤0.008 | ≤0.003 |
| 13 | GBZ 1.0 | ≥190 | <3.00 | <2.00 | <5 | ≤0.008 | ≤0.003 |