Fiberglass Tissue Fiber Glass for Battery Separator Thickness 0.3mm

• Customization: Available
• Shape: Tissue
• Fiber Characteristics: C-Glass
• Model NO.: S-BM0.3
• Diameter of Filaments: Intermediate Fibers
• Fiber Appearance: Continous Fiber
• Glass Composition: C-Glass
• Area Weight: 30G/M2
• Binder Content (%): 16+/-3
• Thicknes: 0.33mm
• Tensile Strength Md(N/50mm): 130
• Acid Resistance 72hours (%): 1.89
• Reductive Kmno4 (Ml/G): 13.25
• Md Tensile Strength(Kn/M): 1.0
• Wetting Time (S): 7.2
• Transport Package: Pallet
• Specification: S-BM
• Origin: China
• HS Code: 70193900
• Production Capacity: 10 Million M2/Month

Product Description

 

Product Description

The battery separator tissue is chiefly used as the base material of lead acid battery separator. 
It is raw material of glass fiber separator, PE+glass separator, PVC+glass separator.
 

Has advantage of good acid resistance, high porosity, small pore size, high liquid absorptivity and low electric resistance.
Good vibrating resistance, starting ability and longer service life.
The surface is flat and smooth, with uniform thickness.
Capable of preventing short circuits and absorbing needed electrolyte. 

Product Parameters

Technical Data:

ITEM	STANDARD VALUE	STANDARD NO	TESTING RESULT
Weight(g/m2)	/	Q/320412 CXB005 --- 2011	33
Binder content (%)	16±3		16.47
Thickness (mm)	0.3±0.03		0.33
Tensile strength Machine direction(N/5cm)	≥60		130
Acid resistance / 72 hours (%)	≤3		1.89
Reductive KmnO4 (ml/g)	≤15		13.25
Wetting time (s)	≤100		7.2

Packing:
The product is wound tightly into a roll on a paper core. Each roll is wrapped into a plastic bag and placed in a carton box.Then put into a pallet.
 
Storage condition:
Unless otherwise specified, it is recommended to store in a cool and dry condition. The product must remain in packaging material until just prior to its use.





Give us a chance, and we' ll return you with satisfaction.