Thermoplastic Prepreg Assembled Fiberglass Roving for Automotive Application
|
Still deciding? Get samples of $ !
Request Sample
|
| Customization: | Available |
|---|---|
| Fiberglass Type: | E-Glass |
| Certification: | RoHS |
Suppliers with verified business licenses
Audited Supplier Audited by an independent third-party inspection agency
Find Similar Products
Basic Info.
- Model NO.
- 60-R-1870N-354
- Fiber Glass Content
- 60%
- Tensile Strength
- 620MPa
- Tensile Modulus
- 33gpa
- Flexural Strength
- 390MPa
- Flexural Modulus
- 25gpa
- Notched Impact
- 370kilojoules Per Square Meter
- Application
- Molding, Pultrusion
- Transport Package
- Pet Film
- Specification
- A Grade
- Trademark
- union
- Origin
- China
- HS Code
- 70191200
- Production Capacity
- 30000 Ton/Year
Product Description
Compofil-PP is a type of thermoplastic prepreg made from continuous fiberglass coated with PP resin. It is specially designed to manufacture high performance PP composite components directly with no need for extra resin.
·Stable thermoplastic prepreg with excellent self-impregnation
·Environment-friendly production process and recyclability
·High productivity and short processing cycle
·High glass fiber content
| Resin type | PP | |
| Typical fiber glass content (%) | 60 | |
| Typical linear density (tex) | 800 / 1870 | |
| Color | N Natural color |
B Black color |
| Example | Compofil-PP-60-R- 1870N-354 | |
| Mechanical properties | Unit | Value | Resin | Test menthod |
| Fiber glass content | % | 60 | PP | GB/T 2577 |
| Tensile strength | MPa | 620 | PP | ISO 527-5 |
| Tensile modulus | GPa | 33 | PP | ISO 527-5 |
| Flexural strength | MPa | 390 | PP | ISO 178 |
| Flexural modulus | GPa | 25 | PP | ISO 178 |
| Notched impact | kJ/m² | 370 | PP | ISO 179 |
·The product is best used within 12 months after production, and should be kept in the original package before use.
·Care should be taken when using the product to prevent it from being scratched or damaged.
·The temperature and humidity of the product should be conditioned to be close or equal to the ambient temperature and
humidity before use, and the ambient temperature and humidity should be properly controlled during the use.
| Item | unit | Standard | |
Typical packaging method |
/ | Packed on pallets. | |
Typical package height |
mm (in) | 260 (10.2) | |
Package inner diameter |
mm (in) | 160 (6.3) | |
Typical package outer diameter |
mm (in) | 275 (10.8) | |
Typical package weight |
Kg (lb) | 10 (22.0) | |
Number of layers |
(layer) | 3 | 4 |
Number of packages per layer |
(pcs) | 16 | |
| Number of packages per pallet | (pcs) | 48 | 64 |
| Net weight per pallet | kg (lb) | 480 (1058.2) | 640 (1411.0) |
| Pallet length | mm (in) | 1140 (44.9) | |
| Pallet width | mm (in) | 1140 (44.9) | |
| Pallet height | mm (in) | 940 (37.0) | 1200 (47.2) |
Unless otherwise specified, the fiberglass products should be stored in a dry,cool and moisture proof area.The best temperature and humidity should be maintained at -10ºC~35ºC and ≤80% respectively. To ensure safety and avoid damage to the product, the pallets should be stacked not more than three layers high. When the pallets are stacked in two or three layers, special care should be taken to correctly and smoothly move the upper pallet.
354 is a Compofil product for fabrics. It is suitable for various composite processes including compression molding, vacuum assisted molding, and pultrusion. Its application fields include aerospace, automotive, construction, sports and new energy
Give us a chance, and we' ll return you with satisfaction.
){kind=link}
Send your message to this supplier
People who viewed this also viewed
Product Groups
Find Similar Products By Category
- Supplier Homepage
- Products
- Woven Roving and Glass Cloth
- Fiber Glass Cloth
- Thermoplastic Prepreg Assembled Fiberglass Roving for Automotive Application