High-Quality 15mm Rigid PVC Foam for Marine Applications

Product Description

Product Description

PVC foam is a cross-linked rigid structural PVC foam material, as a close cell foam, based on vinyl polymer,
modified with the throughout Aramids link. It is the compounding chemical material based on PVC and PUR.
It is said as the cross-linked PVC foam core, in the international practice.It can be used as the core material in the sandwich structure.

 

Product Features

Lightweight and High Strength: Despite its low weight, PVC foam offers exceptional strength, making it an ideal material for applications where both durability and weight reduction are critical.

Excellent Impact Resistance: The foam exhibits superior impact resistance, ensuring long-lasting performance even under harsh conditions.

Chemical Resistance: PVC foam is highly resistant to a wide range of chemicals, making it suitable for environments where exposure to corrosive substances is a concern.

Low Water Absorption: The material's almost negligible water absorption rate ensures stability and performance in humid or wet conditions.

Self-Extinguishing: PVC foam is designed to be self-extinguishing, enhancing safety in applications where fire resistance is crucial.

Thermal and Acoustic Insulation: The foam provides excellent thermal and acoustic insulation properties, making it an ideal choice for applications requiring temperature control and noise reduction.
 

Detailed Photos

 

Product Parameters

 

Item	Standard	Unit		P48	P60	P80	P100	P130	P200	P250
Density	ISO 845	Kg/m^3	msmv	48	60	80	100	130	200	250
Density(Nominal)	ISO 845	Kg/m^3	msv	/	54	72	/	/	/	/
Tensile strength	ASTM C297	Mpa	msv	1.4	1.8	2.5	3.5	4.5	7.1	9.2
Tensile strength	ASTM C297	Mpa	msmv	1.1	1.5	2.2	2.5	3.5	6.3	8
Tensile modulus	ASTM C297	Mpa	msv	55	75	95	130	175	250	360
Tensile modulus	ASTM C297	Mpa	msmv	45	57	85	105	135	210	320
Compressive strength	ISO 844	Mpa	msv	0.6	0.93	1.4	2	3	4.8	6.2
Compressive strength	ISO 844	Mpa	msmv	0.5	0.7	1.15	1.65	2.4	4.2	5.4
Compressive modulus	ISO 844	Mpa	msv	50	70	90	135	170	240	300
Compressive modulus	ISO 844	Mpa	msmv	45	60	80	115	145	200	240
Shear strength	ISO 1922	Mpa	msv	0.5	0.76	1.15	1.44	2.1	3.5	4
Shear strength	ISO 1922	Mpa	msmv	0.46	0.63	0.95	1.4	1.9	3.2	3.9
Shear modulus	ISO 1922	Mpa	msv	15	20	27	35	50	85	104
Shear modulus	ISO 1922	Mpa	msmv	12	16	23	28	40	75	88
Shear elongation,at break	ISO 1922	%	msmv	8	10	15	15	20	20	20
Shear elongation,at break	ISO 1922	%	msv	/	20	30	/	/	/	/

 